Thermal conductivity against densityHigher and further left: spreads more heat for its weightThermal expansion against thermal conductivityLower and further right: warps less when heated
Try it on a partA bracket to run stress or thermal on, free in your browser
VICTREX PEEK 450G Technical Data SheetVictrexPlastic PEEK · Yield strength: typical, tensile yieldPlastic PEEK · Compressive strength: typical, 23 CPlastic PEEK · Flexural strength: typical, flexural stress at yield, 23 CPlastic PEEK · Elongation at break: typical, at breakPlastic PEEK · Young's modulus (stiffness): typical (nominal)Plastic PEEK · Density: typical (crystalline)Plastic PEEK · Thermal conductivity: typical, average, 23 CPlastic PEEK · Thermal expansion: average of flow/cross-flow, below Tg (<143 C)Plastic PEEK · Melting point: typical, DSCPlastic PEEK · Glass transition: onset (midpoint 150 C)Plastic PEEK · Max service temperature: UL 746B RTI, mechanical strength (continuous use index)
3
Engineering Polymers Part and Mold Design: Thermoplastics, A Design GuideCovestroPlastic Nylon · Poisson's ratio: base material: unfilled polyamide (PA), conditioned, maker design-guide family value (Covestro Table 3-1)
4
VICTREX PEEK for Use in Fluid Management (2020)VictrexPlastic PEEK · Poisson's ratio: typical
5
Ultramid (PA) Product RangeBASFPlastic Nylon · Thermal conductivity: base material: unreinforced BASF Ultramid PA66 (A3K) and PA6 (B3S), 23 C (same value for both)Plastic Nylon · Thermal expansion: base material: unreinforced BASF Ultramid PA66 (A3K, 98) and PA6 (B3S, 102), 23-55 CPlastic Nylon · Specific heat: base material: unreinforced BASF Ultramid PA66 (A3K) and PA6 (B3S), 23 C (same value for both)
6
VICTREX PEEK 450G Technical Data Sheet (2012)Victrexarchived copyPlastic PEEK · Specific heat: typical, 23 °C, DSC (Victrex PEEK 450G TDS, revision Jul 2012)
Each number points to the document that states it, with the exact basis. Values without a number are computed from the sourced ones. "Not sourced" means no citable source states it (or only a specification minimum); figures computed from it are left out too.
Plastic Nylon is 3D printed: its properties depend on build direction and print settings; these are typical values.
Questions
Mechanical
Is Plastic Nylon stronger than Plastic PEEK?
Plastic PEEK is stronger: its yield strength is 98 MPa against 63.1 MPa for Plastic Nylon (1.55x).
Which is lighter, Plastic Nylon or Plastic PEEK?
Plastic Nylon is lighter: 1,140 kg/m³ against 1,300 kg/m³ for Plastic PEEK.
Which is stiffer, Plastic Nylon or Plastic PEEK?
Plastic PEEK is stiffer: Young's modulus 4 GPa against 2.33 GPa for Plastic Nylon, so the same part in Plastic PEEK deflects less under the same load.
Which is lighter for the same job, Plastic Nylon or Plastic PEEK?
For the same stiffness or strength: Plastic PEEK is lighter for a stiff rod or tie (tension), stiff beam (bending), stiff panel or plate, strong rod or tie, strong beam, strong panel or plate.
Part that must be
Plastic Nylon
Plastic PEEK
Stiff rod or tie (tension)
1.5x heavier
lighter
Stiff beam (bending)
15% heavier
lighter
Stiff panel or plate
5% heavier
lighter
Strong rod or tie
36% heavier
lighter
Strong beam
18% heavier
lighter
Strong panel or plate
9% heavier
lighter
For the same stiffness or strength, mass scales with density over stiffness (or strength) raised to a power set by how the part is loaded: 1 for a rod in tension, 1/2 for a beam in bending, 1/3 for a panel (the standard material-selection indices).
Thermal
Which conducts heat better, Plastic Nylon or Plastic PEEK?
Plastic Nylon conducts heat better: 0.33 W/m·K against 0.29 W/m·K for Plastic PEEK.
Which expands less with temperature?
Plastic PEEK expands less: 55 µm/m·K against 100 µm/m·K for Plastic Nylon.