Thermal conductivity against densityHigher and further left: spreads more heat for its weightThermal expansion against thermal conductivityLower and further right: warps less when heated
Try it on a partA bracket to run stress or thermal on, free in your browser
Sources4 documents: Outokumpu, ATI, Steel Construction Institute, Carpenter Technology
Stainless Steel 303
1.4305 / UNS S30300, Outokumpu typical values (hot rolled, solution annealed) from 'Steel Grades, Properties and Global Standards'; max service from Carpenter CarTech 303 datasheet
Stainless Steel 316
ATI 316 (UNS S31600), annealed 1.0 mm sheet, ATI technical data sheet (2012); Poisson's ratio from the Nickel Institute/SCI structural stainless design manual
1
Steel Grades, Properties and Global StandardsOutokumpuarchived copyStainless Steel 303 · Yield strength: Outokumpu typical (product P = hot rolled plate, transverse)Stainless Steel 303 · Ultimate tensile strength: Outokumpu typicalStainless Steel 303 · Elongation at break: Outokumpu typical, A5Stainless Steel 303 · Young's modulus (stiffness): at RT (Table 12)Stainless Steel 303 · Density: at RTStainless Steel 303 · Thermal conductivity: at RTStainless Steel 303 · Thermal expansion: mean, 20–100 °CStainless Steel 303 · Specific heat: at RT
2
ATI 316, 316L, 317 and 317L Technical Data Sheet (2012)ATIarchived copyStainless Steel 316 · Yield strength: typical (representative), annealed 1.0 mm sheetStainless Steel 316 · Ultimate tensile strength: typical (representative), annealed 1.0 mm sheetStainless Steel 316 · Elongation at break: typical (representative), annealed, in 2 in. (51 mm)Stainless Steel 316 · Young's modulus (stiffness): typical, in tensionStainless Steel 316 · Density: typicalStainless Steel 316 · Thermal conductivity: 20–100 °CStainless Steel 316 · Thermal expansion: mean, 20–100 °CStainless Steel 316 · Specific heat: at 20 °CStainless Steel 316 · Melting point: melting rangeStainless Steel 316 · Max service temperature: oxidation (scaling) limit in air
3
Design Manual for Structural Stainless Steel, 4th Edition (P413)Steel Construction Institutearchived copyStainless Steel 303 · Poisson's ratio: design value (structural stainless steels)Stainless Steel 316 · Poisson's ratio: design value (structural stainless steels)
4
Carpenter Stainless Type 303 Data SheetCarpenter Technologyarchived copyStainless Steel 303 · Max service temperature: continuous, scaling limit
Each number points to the document that states it, with the exact basis. Values without a number are computed from the sourced ones. "Not sourced" means no citable source states it (or only a specification minimum); figures computed from it are left out too.
Questions
Mechanical
Is Stainless Steel 303 stronger than Stainless Steel 316?
Stainless Steel 303 is stronger: its yield strength is 275 MPa against 265 MPa for Stainless Steel 316 (4%).
Which is lighter, Stainless Steel 303 or Stainless Steel 316?
Stainless Steel 303 is lighter: 7,900 kg/m³ against 8,027 kg/m³ for Stainless Steel 316.
Which is stiffer, Stainless Steel 303 or Stainless Steel 316?
Stainless Steel 303 is stiffer: Young's modulus 200 GPa against 200 GPa for Stainless Steel 316, so the same part in Stainless Steel 303 deflects less under the same load.
Which is lighter for the same job, Stainless Steel 303 or Stainless Steel 316?
For the same stiffness or strength: Stainless Steel 303 is lighter for a stiff rod or tie (tension), stiff beam (bending), stiff panel or plate, strong rod or tie, strong beam, strong panel or plate.
Part that must be
Stainless Steel 303
Stainless Steel 316
Stiff rod or tie (tension)
lighter
2% heavier
Stiff beam (bending)
lighter
2% heavier
Stiff panel or plate
lighter
2% heavier
Strong rod or tie
lighter
5% heavier
Strong beam
lighter
4% heavier
Strong panel or plate
lighter
4% heavier
For the same stiffness or strength, mass scales with density over stiffness (or strength) raised to a power set by how the part is loaded: 1 for a rod in tension, 1/2 for a beam in bending, 1/3 for a panel (the standard material-selection indices).
Which is more ductile, Stainless Steel 303 or Stainless Steel 316?
Stainless Steel 316 stretches further before it breaks: 61% elongation at break against 35% for Stainless Steel 303.
Thermal
Which conducts heat better, Stainless Steel 303 or Stainless Steel 316?
Stainless Steel 303 conducts heat better: 15 W/m·K against 14.6 W/m·K for Stainless Steel 316.
Which expands less with temperature?
Stainless Steel 303 expands less: 16 µm/m·K against 16.5 µm/m·K for Stainless Steel 316.