Thermal conductivity against densityHigher and further left: spreads more heat for its weightThermal expansion against thermal conductivityLower and further right: warps less when heated
Try it on a partA bracket to run stress or thermal on, free in your browser
BASF Ultradur B 4300 G6 (PBT, 30% glass fibre), injection moulding grade; product information sheet 09/2026, typical values for uncoloured product at 23 °C.
Plastic UHMWPE
Celanese GUR 4120 (avg. molecular weight 4.7x10^6 g/mol), typical values on compression-molded specimens; CTE and thermal conductivity from Celanese's generic UHMWPE guide (grade not named)
1
GUR UHMW-PE Overview (GUR-015)CelanesePlastic UHMWPE · Yield strength: typical, tensile stress at yield ISO 527, 50 mm/minPlastic UHMWPE · Ultimate tensile strength: typical, tensile stress at break ISO 527, 50 mm/minPlastic UHMWPE · Elongation at break: typical, nominal elongation at break ISO 527Plastic UHMWPE · Young's modulus (stiffness): typical, tensile modulus ISO 527, 1 mm/minPlastic UHMWPE · Density: typicalPlastic UHMWPE · Melting point: DSC 10 K/minPlastic UHMWPE · Max service temperature: recommended max constant operating temperature
2
Ultradur B 4300 G6 Product InformationBASFPlastic PBT GF30 · Ultimate tensile strength: stress at break, 23 °CPlastic PBT GF30 · Flexural strength: typical, 23 °CPlastic PBT GF30 · Elongation at break: strain at break, 23 °CPlastic PBT GF30 · Young's modulus (stiffness): typical, 23 °CPlastic PBT GF30 · Density: typicalPlastic PBT GF30 · Thermal conductivity: typical (DIN 52612-1)Plastic PBT GF30 · Thermal expansion: longitudinal (flow), mean 23-55 °CPlastic PBT GF30 · Specific heat: typical, 23 °CPlastic PBT GF30 · Melting point: DSC (ISO 11357)Plastic PBT GF30 · Max service temperature: HDT 1.8 MPa
3
GUR UHMW-PE Polymer Guide (GUR-003)Celanesearchived copyPlastic UHMWPE · Thermal conductivity: typical, unfilled (narrative value, generic Celanese UHMWPE)Plastic UHMWPE · Thermal expansion: typical, 20 to 100 °C (generic Celanese UHMWPE)
Each number points to the document that states it, with the exact basis. Values without a number are computed from the sourced ones. "Not sourced" means no citable source states it (or only a specification minimum); figures computed from it are left out too.
Questions
Mechanical
Is Plastic PBT GF30 stronger than Plastic UHMWPE?
Plastic PBT GF30 is stronger: its tensile strength is 140 MPa against yield strength 20 MPa for Plastic UHMWPE (7x).
Which is lighter, Plastic PBT GF30 or Plastic UHMWPE?
Plastic UHMWPE is lighter: 930 kg/m³ against 1,530 kg/m³ for Plastic PBT GF30.
Which is stiffer, Plastic PBT GF30 or Plastic UHMWPE?
Plastic PBT GF30 is stiffer: Young's modulus 9.8 GPa against 0.66 GPa for Plastic UHMWPE, so the same part in Plastic PBT GF30 deflects less under the same load.
Which is lighter for the same job, Plastic PBT GF30 or Plastic UHMWPE?
For the same stiffness or strength: Plastic PBT GF30 is lighter for a stiff rod or tie (tension), stiff beam (bending), stiff panel or plate, strong rod or tie, strong beam, strong panel or plate.
Part that must be
Plastic PBT GF30
Plastic UHMWPE
Stiff rod or tie (tension)
lighter
9.03x heavier
Stiff beam (bending)
lighter
2.34x heavier
Stiff panel or plate
lighter
49% heavier
Strong rod or tie
lighter
4.25x heavier
Strong beam
lighter
2.22x heavier
Strong panel or plate
lighter
1.61x heavier
For the same stiffness or strength, mass scales with density over stiffness (or strength) raised to a power set by how the part is loaded: 1 for a rod in tension, 1/2 for a beam in bending, 1/3 for a panel (the standard material-selection indices).
Which is more ductile, Plastic PBT GF30 or Plastic UHMWPE?
Plastic UHMWPE stretches further before it breaks: 465% elongation at break against 3% for Plastic PBT GF30.
Thermal
Which conducts heat better, Plastic PBT GF30 or Plastic UHMWPE?
Plastic UHMWPE conducts heat better: 0.4 W/m·K against 0.27 W/m·K for Plastic PBT GF30.
Which expands less with temperature?
Plastic PBT GF30 expands less: 25 µm/m·K against 200 µm/m·K for Plastic UHMWPE.