Thermal conductivity against densityHigher and further left: spreads more heat for its weightThermal expansion against thermal conductivityLower and further right: warps less when heated
Try it on a partA bracket to run stress or thermal on, free in your browser
Ultimaker Nylon, 3D-printed specimens, XY (flat), conditioned >=24 h at room temperature; Ultimaker S5 Pro, engineering intent profile, 0.15 mm layer height, AA 0.4 print core, 100% infill, Cura 4.9, printed one-at-a-time, conditioned >=24 h at room temperature. TDS v2.00, April 20, 2022.
Plastic PBT GF30
BASF Ultradur B 4300 G6 (PBT, 30% glass fibre), injection moulding grade; product information sheet 09/2026, typical values for uncoloured product at 23 °C.
Ultradur B 4300 G6 Product InformationBASFPlastic PBT GF30 · Ultimate tensile strength: stress at break, 23 °CPlastic PBT GF30 · Flexural strength: typical, 23 °CPlastic PBT GF30 · Elongation at break: strain at break, 23 °CPlastic PBT GF30 · Young's modulus (stiffness): typical, 23 °CPlastic PBT GF30 · Density: typicalPlastic PBT GF30 · Thermal conductivity: typical (DIN 52612-1)Plastic PBT GF30 · Thermal expansion: longitudinal (flow), mean 23-55 °CPlastic PBT GF30 · Specific heat: typical, 23 °CPlastic PBT GF30 · Melting point: DSC (ISO 11357)Plastic PBT GF30 · Max service temperature: HDT 1.8 MPa
3
Engineering Polymers Part and Mold Design: Thermoplastics, A Design GuideCovestroPlastic Nylon · Poisson's ratio: base material: unfilled polyamide (PA), conditioned, maker design-guide family value (Covestro Table 3-1)
4
Ultramid (PA) Product RangeBASFPlastic Nylon · Thermal conductivity: base material: unreinforced BASF Ultramid PA66 (A3K) and PA6 (B3S), 23 C (same value for both)Plastic Nylon · Thermal expansion: base material: unreinforced BASF Ultramid PA66 (A3K, 98) and PA6 (B3S, 102), 23-55 CPlastic Nylon · Specific heat: base material: unreinforced BASF Ultramid PA66 (A3K) and PA6 (B3S), 23 C (same value for both)
Each number points to the document that states it, with the exact basis. Values without a number are computed from the sourced ones. "Not sourced" means no citable source states it (or only a specification minimum); figures computed from it are left out too.
Plastic Nylon is 3D printed: its properties depend on build direction and print settings; these are typical values.
Questions
Mechanical
Is Plastic Nylon stronger than Plastic PBT GF30?
Plastic PBT GF30 is stronger: its tensile strength is 140 MPa against yield strength 63.1 MPa for Plastic Nylon (2.22x).
Which is lighter, Plastic Nylon or Plastic PBT GF30?
Plastic Nylon is lighter: 1,140 kg/m³ against 1,530 kg/m³ for Plastic PBT GF30.
Which is stiffer, Plastic Nylon or Plastic PBT GF30?
Plastic PBT GF30 is stiffer: Young's modulus 9.8 GPa against 2.33 GPa for Plastic Nylon, so the same part in Plastic PBT GF30 deflects less under the same load.
Which is lighter for the same job, Plastic Nylon or Plastic PBT GF30?
For the same stiffness or strength: Plastic PBT GF30 is lighter for a stiff rod or tie (tension), stiff beam (bending), stiff panel or plate, strong rod or tie, strong beam, strong panel or plate.
Part that must be
Plastic Nylon
Plastic PBT GF30
Stiff rod or tie (tension)
3.13x heavier
lighter
Stiff beam (bending)
1.53x heavier
lighter
Stiff panel or plate
20% heavier
lighter
Strong rod or tie
1.65x heavier
lighter
Strong beam
27% heavier
lighter
Strong panel or plate
11% heavier
lighter
For the same stiffness or strength, mass scales with density over stiffness (or strength) raised to a power set by how the part is loaded: 1 for a rod in tension, 1/2 for a beam in bending, 1/3 for a panel (the standard material-selection indices).
Thermal
Which conducts heat better, Plastic Nylon or Plastic PBT GF30?
Plastic Nylon conducts heat better: 0.33 W/m·K against 0.27 W/m·K for Plastic PBT GF30.
Which expands less with temperature?
Plastic PBT GF30 expands less: 25 µm/m·K against 100 µm/m·K for Plastic Nylon.